Description
PR-2870 Class A is a light weight, non-chromate corrosion inhibitive sealant. It has a service temperature range from -80°F (-62°C) to 250°F (121°C), with intermittent excursions up to 300°F (149°C).
This material acts as an effective corrosion inhibitor when used with aluminum alloys or with dissimilar metals. The cured sealant maintains elastomeric properties after limited exposure to both jet fuel and aviation gas. PR-2870 Class A is a two-part, epoxy cured PERMAPOL® P-3.1 polythioether compound.
The uncured material is suitable for application by brush up to a thickness of 25 mils. It cures at room temperature to form a resilient sealant having excellent adhesion to common aircraft substrates.
Surface preparation
Immediately before applying sealant to primed substrates, the surfaces should be cleaned with solvents. Contaminants such as dirt, grease, and/or processing lubricants must be removed prior to sealant application.
A progressive cleaning procedure should be employed using appropriate solvents and a new lint-free cloth conforming to AMS 3819. (Reclaimed solvents or tissue paper should not be used.) Always pour solvent on the cloth to avoid contaminating the solvent supply.
Wash one small area at a time. It is important that the surface is dried with a second clean cloth prior to the solvent evaporating to prevent the redeposition of contaminants on the substrate. Substrate composition can vary greatly.
This can affect sealant adhesion. It is recommended that adhesion characteristics to a specific substrate be determined prior to application on production parts or assemblies.